Effect of Internal Curing On Mechanical Properties and Durability of High-Strength Concretes

Authors
J. Ahmadi
A. Panahi
Abstract
HPC has become popular due to its superior mechanical and
durability properties.HPC significantly reduces maintenance
costs and enhances service life.
Internal curing of high performance concrete (HPC) by pre-saturated lightweight aggregates is a wellestablished
method of counteracting self-desiccation and autogenous shrinkage. However, by introducing the
internal water reservoirs strength and durability properties can be injured.
Concrete is a strong and durable material that has been utilized since the beginning of
civilization. It is understood that many of the early structures are deteriorating or have
already deteriorated away; however, with the knowledge of the material properties of
concrete that is available, it is hard to imagine that concrete structures is prematurely failing
before their intended service life. There are many factors involved in these failures, some of
which are due to environmental conditions and others which have arisen from human errors
or lack of knowledge.
Early age properties of concrete are vital to its long-term performance. Many
contractors and owners are interested only on the strength of concrete in 28 days or 90 days,
that they overlook the importance of other early age issue especially when the mix design has
water to cementitious material ratio (w/cm) lower than ~0.42.
Internal curing with LWA has been successfully used recently in large construction projects
of normal density concrete structures. For example, in January 2005, about 190 000 m
of
internally-cured concrete was used in a large paving project in Hutchins, Texas.
Although the benefits of internal curing for high-performance concrete structures have been
evidenced in the laboratory and some field investigations (such as those previously
mentioned), the literature does not provide any significant quantitative information regarding
the additional extension of the service life that can be achieved by the use of internal curing
in concrete structures.
A great concern for design engineers and contractors is whether the concrete will achieve the
specified compressive strength and all durability requirements in the structure during service.
Cusson & Hoogeveen (2008) demonstrated that internal curing can reduce autogenous
shrinkage considerably without affecting the strength and stiffness of high-performance
concrete. This was achieved by reducing the amount of mix water in the concrete by an
amount equal to that used in the LWA for internal curing, thus reducing the effective watercement
ratio
(w/c
) of the concrete when using higher quantities of pre-soaked LWA.
Tests by the widely accepted
methods of durability assessment, such as resistance to chloride penetration, air permeability, water
absorption, autogenous and drying shrinkage and mass loss, were conducted on HPC mixes made at water to
cement ratios in the range of 0.21–0.33. The effect of internal curing on the durability related properties of
high-performance concretes as a function of water to cement ratio is reported.

Keywords

[1] K.W.  Meeks, N.J. Carino, “Curing of High-Performance Concrete: Report of the State-of-the-Art,” NISTIR 6295, 1999.
[2] A.I. Neville, P.C. Aïtcin, High performance concrete—an overview, Mater. Struct. 31 (1998) 111–117.
[3] S. Zhutovsky, K. Kovler, Effect of internal curing on durability-related properties of high performance concrete, Cem & Conc research. 42 (2012) 20–26
[4] D.P.  Bentz, K.A.  Snyder, P.E.  Stutzman, Microstructural Modeling of   Self- Desiccation During Hydration, Lund, Sweden, in:  B. Persson, G. Fagerlund (Eds.), Proceeding of an Int. Research Seminar Self-Desiccation and Its Importance in Concrete Technology, 1997, pp.  132–140.
[5] A. Bentur, S. Igarashi, K. Kovler, Control of autogenous shrinkage stresses and cracking in high strength concretes, Proc.  of 5th Int.  Symp. of High Strength/High Performance Concrete Sandefjord, Norway, 1999, pp.  1017–1026.
[6] P. Lura, K. van Breugel, Moisture exchange as a basic phenomenon to understand volume changes of lightweight aggregate concrete at early age, in:  V. Baroghel- Bouny, P.C. Aitcin (Eds.), Proc. Int. Workshop on Shrinkage of Concrete Paris, 2000, pp.  533–546.
[7] S.  Zhutovsky, K.  Kotler, A.  Bentur, Influence of wet lightweight aggregate on autogenous shrinkage of concrete at early ages, in: F.-J.  Ulm, Z.P.  Bazant, F.H. Wittmann (Eds.), Proc. 6th Int. Conf. Creep, Shrinkage and Durability Mechanics of Concrete and Other Quasi-Brittle materials Cambridge (MA), USA, 2001, pp. 697–702.
[8] RILEM TC-196, Internal Curing of Concrete, State-of-the-Art Report of RILEM Technical Committee 196-ICC, in: K. Kovler, O.M.  Jensen (Eds.), RILEM Publications S.A.R.L, France, Bagneux, 2007, 139 pp.
[9] P. Schwesinger, G. Sickert, reducing shrinkage in HPC by internal curing by using pre-soaked LWA, Proc.   Int.   Workshop on   Control of   Cracking in   Early-Age Concrete, Tohoku University, Japan, 2000, pp.  313–318.
 
[10] K. van Breugel, H. Outwerk, J. de Vries, Effect of mixture composition and size effect on shrinkage of high strength concrete, in:  V. Baroghel-Bouny, P.C. Aitcin (Eds.), Proc.  Int.  Workshop on Shrinkage of Concrete Paris, 2000, pp.  161–177.
[11] S. Zhutovsky, K. Kovler, A. Bentur, Efficiency of lightweight aggregates for internal curing of high strength concrete to eliminate autogenous shrinkage, RILEM Int.  Conf.  on Early Age Cracking in Cementitious Systems, 2001, pp.  365–374.
[12] O.M. Jensen,P.F.  Hansen, Water-entrained cement-based materials, principles and theoretical background, Cem. Concr. Res. 31 (2001) 647-654.
[13] O.M.  Jensen, P.F.  Hansen, Water-entrained cement-based materials II:  experi- mental observations, Cem.  Concr. Res. 32 (2002) 973–978.
[14] I.  Maruyama, R.  Sato, a trial of reducing autogenous shrinkage by   recycled aggregate, Gaithersburg (MD), USA, in:  B. Persson, D.P. Bentz, L.O. Nilsson (Eds.), Proc.  4th Int. Sem.  on Self-Desiccation and Its Importance in Concrete Technology,2005, pp.  264–270.
[15] T.W.  Bremner, T.A. Holm, Elastic compatibility and the behaviour of concrete, J. Am. Concr. I. 83 (1986) 244–250.
[16] T.A. Holm, O.S. Ooi, T.W.  Bremner, Moisture dynamics in lightweight aggregate and concrete, in:  J.P. Ries, T.A. Holm (Eds.), Theodore Bremner Symp. on High- Performance Lightweight Concrete, Proc.  6th Int, Conf.  on Durability of Concrete, Thessalonika, Greece, 2003, pp.  167–184.
[17] K.S. Chia, M. Zhang, Water permeability and chloride penetrability of high-strength lightweight aggregate concrete, Cem.  Concr. Res. 32 (2002) 639–645.
[18] H. Lam, R.D. Hooton, Effects of internal curing methods on restrained shrinkage and permeability, Gaithersburg (MD), USA, in:  B. Persson, D.P. Bentz, L.O. Nilsson (Eds.), Proc.   4th Int.  Sem.   on Self-Desiccation and Its Importance in Concrete Technology, 2005, pp.  210–228.
[19] D. Cusson, Z. Lounis, L. Daigle, Benefits of internal curing on service life and life- cycle cost of high-performance concrete bridge decks—a case study, Cem.  Concr. Comp. 32 (2010) 339–350.
[20] E. Tazawa, Y. Matsuoka, S. Miyazawa, S. Okamoto, Effect of Autogenous Shrinkage on Self Stress in Hardening Concrete, Munich, Germany, in:  R. Springenschmidt (Ed.), Proc.  of Int. RILEM Symp. Thermal Cracking in Concrete at Early Ages, 1994, pp.  220–228.
[21] A.M. Vaysburd, Durability of lightweight concrete bridges in severe environments, Concr. Int.  18 (1996) 33–38.
[22] Bagery. A, Zanganeh.H, the Comparison of RCMT, RCPT and electrical resistance methods for evaluation of chloride penetration resistance in concrete, Modares Civil Engineering Journal, V 12, 2012 (In Persian).
Modares Civil Engineering journal
Volume 17, Issue 3
September and October 2017
Pages 1-8