Effect of Nano-SiO2 and Silica Fume on Durability of High Strength Concretes under Sulfuric Acid Attack

Authors
H. Rahmani 1
M. Jokar 2
M. Parvinnia 3
1 Civil Engineering Department- yasouj University
2 MSc student, Yasouj university
3 Faculty, Yasoujj university
Abstract
Concrete is one of the most practical and durable construction materials due to economic aspects, abundance of the constituents, adaptability with the environment and its high compressive strength and durabity. High strength concretes are used in the most substructure constructions such as bridges, dams, towers, silos and etc. . The selection of proper aggregates and the constituents affects on the concrete properties such as strength, permeability, and durability. Therefore, optimization of mix designs is necessary to produce high strength and low permeability concretes. Although most of the concrete structures are constructed for 50 years sevice life, however, some of them are sometimes damaged due to sulfuric acid attack. The rate of concrete corrosion in sulfuric acid is a process of dissolution, sedimentation and leaching depends on the chemical compounds of cement, paste reactivity, aggregates type and their grading curves and the proportion of concrete components. Moreover, wetting and drying cycles increases the acid penetration and consequently the rate of corrosion. Remarkable concrete damages have been reported in Australia, Japan, the countries around Persian Gulf, Germany, South Africa and U.S.A.. Therefore, It will be necessary to repair or replace the damaged structure after the attack and it would be very expensive and creates many social problems. Nevetheless, several reports have been published to investigate plain concretes durability in acidic environments, but first, the results are paradoxical for example, silica fume effect against sulfuric acid attack and second, their studies have been conducted on the native construction materials such as fly ash or blast furnace slag. Therefore, it seems necessary to investigate concrete durability against sulfuric acid attack by using new materials such as nano-SiO2. In the present study, durability of concretes containing silica fume, nano-SiO2 and ultra fine Quartz powder was investigated under sulfuric acid attack. Concrete samples of four mix designs, including Silica Fume, nano-SiO2 and ultra fine Quartz powder as cement filler, were investigated to find optimum content of Silica Fume and nano-SiO2. Also to obtain a high strength concretes, ideal grading curve of aggregates and cementitious materials were used which lead to decrease cement consumption. Results show that the very low porosity concretes were obtained based on water absorption test results in comparison to plain concretes. Also, the 28 days compressive strength of all mixtures were obtaied more than 500 kg/cm2 using no more than 325 kg/m3 cementitious material content. Moreover, the durability of concretes against sulfuric acid attack, which is increased by silica fume and nano-SiO2, directly related to the 90 days water absorption. In addition, After 6 months of immersion in sulfuric acid solution with pH of 1.0, the mixture containing 8% silica fume, 2% nano-SiO2 and 25% ultra fine Quartz powder showed the best performance.

Keywords

[1]      D. K. Thistlethwayte, “The Control Of Sulphides In Sewage Systems’’, Butterworths, Sydney, 1972.
[2]      T. Mori, T. Nonaka, K. Tazaki, M. Koga, Y. Hikosaka, S. Noda, ’’Interactions of nutrients, Moisture And pH on Microbial Corrosion of Concrete Sewer Pipes,’’ Water Research 26(1), 1992, pp. 29-37.
[3]      H. Saricimen, M. Maslehuddin, ’’Case Study of Deterioration of Concrete in Sewerage Environment in an Arabian Gulf Country’’, Durability of Building Materials, Vol. 5, 1987, pp. 145-154.
[4]      W. Sand, E. Bock, ’’Concrete corrosion in the Hamburg sewer system’’, Environmental Technology Letters, Vol. 5, 1984, pp. 517– 528.
[5]      J. L. Barnard, ’’Corrosion of sewers’’, Council for Scientific and Industrial Research (CSIR), Research Report 250, South Africa, 1967.
[6]      S. L. Sarkar, ’’Lift stations—a testing ground for concrete durability’’, Concrete Durability, SP-170-69, in: V.M. Malhotra (Ed.), 1997, pp. 1357–1378.
[7]      C. Parker, “The Corrosion Of Concrete Isolation of a Species of Bacterium Associated with the Corrosion of Concrete Exposed to Atmospheres Containing Hydrogen Sulfide.” Australian Journal of Experimental Biology and Medical Science, Vol. 23, No. 3, 1945, pp. 14-17.
[8]      E. Hewayde, M. Nehdi, E. Allouche, G. Nakhla, ”Effect of Mixture Design Parameters and Wetting-Drying Cycles on Resistance of Concrete to Sulfuric Acid Attack”, Journal of Materials in Civil Engineering, Vol. 19. 2007, pp 155-163.
[9]      E.K. Attiogbe, S.H. Rizkalla, “Response of concrete to sulfuric acid attack”, ACI Material Journal, 84, Vol. 6, 1988, pp. 481- 488.
[10]   J. M. Tulliani, L. Montanaro, A. Negro, and M. Collepard, ,” Sulfate Attack of Concrete Building Foundations Induced by Sewage Waters”, Cement and Concrete Research, Vol. 32, 2002, pp. 843-849.
[11]   F.F.Wafa, “Accelerated sulfate attack on concrete in a hot climate”, Cement and Concrete Aggregates, 16 (1), 1994, pp. 31-35,.
[12]   V. Pavlı´k, “Corrosion of hardened cement paste by acetic and nitric acids: Part I. Calculation of corrosion depth”, Cement and Concrete Research, 24, 1994, pp. 551– 562.
[13]   V. Pavlı´k, “Corrosion of hardened cement paste by acetic and nitric acids: Part II. Formation and chemical composition of the corrosion products layer”, Cement and Concrete Research, 24, 1994, pp. 1495–1508.
[14]   J. Monteny, E. Vincke, A. Beeldens, N. D. belie, L. Taerwe, D. V. Gemert, and W. Vestraete, ”Chemical, Microbiological, and in situ Test Methods for Biogenic Sulfuric Acid Corrosion of Concrete”, Cement and Concrete Research, Vol. 30, No. 4, pp. 623-634, 2000.
[15]   J. Monteny, N. D. Belie, E. Vincke,  W. Verstraete, and L. Taerwe, “Chemical and Microbiological Tests to Simulate Sulfuric Acid Corrosion of Polymer-Modified Concrete”, Cement and Concrete Research, Vol. 31, No. 9, 2001, pp. 1359-1365.
[16]   M. L. Brendt, “Protection of Concrete in Cooling Towers from Microbiologically Influence Corrosion.” Geothermal Resources Council Transaction, San Diego, Vol. 25, 2001, pp. 3-7.
[17]   Z.T. Chang, X. J. Song, R. Munn, and M. Marosszeky, “Using limestone aggregates and different cements for enhancing resistance of concrete to sulphuric acid attack”, Cement and Concrete Research 35, 2005, pp. 1486– 1494.
[18]   V. Pavlı´k, S. Uncik, “The rate of corrosion of hardened cement pastes and mortars with additive of silica fume in acids”, Cement and Concrete Research, 27, 1997, pp. 1731– 1745.
[19]   H. Dorner, “Acid resistance of high performance concrete”, 38th Research colloquium, German Committee for Reinforced Concrete, Munich, Germany, 2000, pp. 77– 86.
[20]   A. A. Ramzanianpour, H. Rahmani,” Effect of Silica fume and Ultra Fine Filler on Acid Resistance of Concrete”, Iranian Corrosion/ICA International Congress, 14-15 May; Tehran, Iran, 2007.
[21]   H. Rahmani, A. A. Ramazanianpour, “effect of Binary Cement Replacement Materials on Sulfuric Acid Resistance of Dense Concretes”. Magazine of Concrete Research, No. 2, 2008, pp. 145-155.
[22]   W. J. Byung, H. K. Chang, H. T. Ghi, B. P. Jong, “Characteristics of cement mortar with nano-SiO2 particles”, Construction And Building Materials, Vol. 21, 2007, pp. 1351-1355.
[23]   K.L. Lin,  W.C. Chang,  D.F. Lin, H.L. Luo, M.C. Tsai, "Effects of nano-SiO2 and different ash particle sizes on sludge ash", Cement Mortar Journal of Environmental Management, 88, 2008, 708–714.
[24]   B. H. A. Hillemeier, "High Performance Concrete Specialized for Acid Resistance", First International Conference on Concrete & Development, Tehran, Iran, 2001.
 
 
 
 
 
 
 
 
 
 
[25]   M. Jokar, H. Rahmani, M. Parvinnia, "Ideal Grading of Dense Packed Concrete", 1st National Conferece in non Osmosis Concretes - Water Storage Tank, Rasht, Iran, 2011.
[26]   Q. Niu, “Effect of Superfine Slag Powder on Cement Properties”, Cement and Concrete Research, Vol. 32, pp. 615-621, 2002.
[27]   L. Jianyong, T. Pei, “Effect of Slag and Silica Fume on Mechanical Properties of High Strength Concrete”, Cement and Concrete Research, 27-2, 833, 1997.
[28]   R. K. Iler, “The chemistry of silica, solubility, polymerization, colloid and surface properties, and biochemistry of silica”, 1979, John Wiley.
[29]   E. Pelizzetti, “Fine particles science and technology: from micro to nanoparticles”, Kluwer Academic Publishers, 1996.
[30]   T. Sugimoto “Fine particles: synthesis, characterization, and mechanisms of growth”, Volume 92, Surfactant Science Series, 2000.
[31]   K. Fukushi, T. Sato, “Using a surface complexation model to predict the nature and stability of nanoparticles”. Environtal Science and Technology, 39, 2008, pp.1250–6.
[32]   Y. Qing, Z. Zenan, K. Deyu, C. Rongshen, “Influence of nano-SiO2 addition on properties of hardened cement paste as compared with silica fume”, Construction Building Material, vol. 21(3), 2007, pp. 539–545.
[33]   L. Senff, A.J. Labrincha, M.V. Ferreira, D. Hotza, W. L. Repette, “Effect of nano-silica on rheology and fresh properties of cement pastes and mortars”, Construction and Building Materials, 23, 2009, pp. 2487-2491.
 
 
Modares Civil Engineering journal
Volume 15, Issue 2
July and August 2015
Pages 1-12