دانشگاه تربیت مدرس مهندسی عمران مدرس 2476-6763 12 4 2012 11 21 Property Improvement of Iranian LWAC: Investigation of Mechanical Properties and Stress-Strain Curve بررسی مشخصات مکانیکی و منحنی تنش- کرنش بتن سبک‌دانه موجود در ایران 79 89 11562 FA مصطفی خانزادی دانشگاه علم و صنعت ایران علیرضا چاله‌کایی دانشگاه علم و صنعت ایران Journal Article The potential use of leca and scoria aggregates available in Iran to produce high strength lightweight concrete has been studied. As a result of various concrete mixes with different lightweight aggregate amount, and using normal techniques, it was possible to obtain high quality lightweight concrete which is suitable for application in reinforced and prestressed concrete structures.In order to investigate the mechanical short term properties of this type of high strength concrete, different tests had done. The properties obtained include unit weight, compressive strength, static modulus of elasticity and poisson's ratio.Among the 28 day aged tested specimens, we could produce HSLWC containing scoria with 55 MPa compressive strength and 2070 kg/m³ weight.In LWC containing leca, a cube compressive strength of about 41 MPa with a unit weight of 1865 kg/m³ was reported.Static modulus of elasticity in concretes containingleca was between 15 to 19 GPa. It was between 17 to 19.5 GPa forconcretescontainingscoria. Some equations were offered to estimate static modulus of elasticity of these concretes based on their compressive strength and unit weight. The mechanical properties were improved by reducing the amount of lightweight aggregate. The results show that both scoria and leca were effective in improving the mechanical properties, but scoria could reach superior limits.Stress- strain curves of investigated concretes were studied and some recommendations are presented for estimating the curves.Stress-strain curves of investigated concretes are almost linear in ascending and descending branch.According to the observed coefficients, withincrease in concrete strength, the slope of the curve is reducedin comparison with modulus of elasticity. For scoria, the slope of curve is lower than modulus in all three mix designs, because of the higher modulus of elasticity of scoria aggregates, in comparison with leca. - در این پژوهش امکان استفاده از سنگدانه های اسکوریا و لیکای موجود در کشور برای تولید بتن سبک دانه پرمقاومت بررسی شده است. براساس طرح های گوناگون اختلاط و روش های مرسوم، تولید بتن سبک دانه ای با مقاومت فشاری 28 روزه ی بیشتر از 40 مگاپاسکال که بتوان آن را در بتن مسلح به کار برد، ممکن شد. برای بررسی مشخصات مکانیکی کوتاه مدت این بتن، آزمایش های مختلفی چون وزن مخصوص بتن، مقاومت فشاری، مدول الاستیسیته استاتیکی و ضریب پواسون انجام شد؛ روابطی نیز برای پیش بینی مدول الاستیسیته استاتیکی این بتن ها براساس مقاومت فشاری و وزن مخصوصشان در سن 28 روز ارائه شده است. مشخص شد که با افزایش وزن بتن با تغییر در بافت دانه بندی، مقاومت فشاری و مدول الاستیسیته بتن های آزمایش شده، افزایش یافته است. استفاده از دوده سیلیسی نیز در بهبود مقاومت فشاری این بتن ها مؤثر بوده است. نتایج نشان می دهند که اسکوریا و لیکا در بهبود مشخصات مکانیکی نمونه ها مؤثر بوده که اسکوریا به نتایج مناسب تری رسیده است. منحنی تنش- کرنش بتن های مطالعه شده بررسی شد و توصیه هایی برای تخمین این منحنی ها ارائه شد. بر اساس نتایج، منحنی ها در شاخه های صعودی و نزولی تقریباً خطی بودند. https://mcej.modares.ac.ir/article_11562_673de96b04fa3adcae1aacda704217ef.pdf